Parameters
-
Comments
| Al2O3: | 40% | ZrO2: | 34% |
|---|---|---|---|
| SiO2: | 14% | Na2O: | 1.6% |
| Bulk Density: | 3.95g/cm3 | Certificate: | CE |
| Origin: | China |
AZS 33 Zirconia Corudum Fire Clay Bricks For Glass Furnace , High Strength
Future
1 .Casted by melting raw material in the mold, then cooling and solidification.
2. Strong glass corrosion resistance and high thermal shack stability.
3. Good wear-resistance,dregs-resistance and alkali corrosion resistance.
4. High-purity raw material, barely no pollution.
5. Top quality, long service time.
Specification
| Reference Index | AZS-33# | AZS-36# | AZS-41# | |
| Chemical Composition | Al2O3 | — | — | — |
| ZrO2 | 32-34% | 35-37% | 40-42% | |
| SiO2 | ≤16.0% | ≤14% | ≤13.0% | |
| Na2O | ≤1.5% | ≤1.6% | ≤1.3% | |
| Fe2O3+TiO2+CaO +Ma2O+K2O+B2O3 |
≤2.5% | ≤2.5% | ≤2.5% | |
| Bulk density( Dense part) | 3.85g/cm3 | 3.95g/cm3 | 4.0g/cm3 | |
| Corrosion resistance of glass melt (common glass,1500℃*36h) |
≤1.6mm/24h | ≤1.5mm/24h | ≤1.3mm/24h | |
| Bubbling separate (common glass,1300℃*10h) |
≤2.0% | ≤1.5% | ≤1.3% | |